Quality values.
ABS
| Units | Test methods | Injection moulding | Extrusion | Hard inflamm-able | Glass-rein-forced | ||||
|---|---|---|---|---|---|---|---|---|---|
| ABS 412Ì | ABS 47KS | ABS 456K | ABS 438K | ABS 465KE | ABS 475KE | ABS 426ÊF | ABS 415G | ||
| Melt flow index (200°Ñ, 10 kg) | |||||||||
| g/10 min | GOST 11645-73 ASTM D-1238 | 12÷15 | 15÷18 | 10÷12 | 15÷18 | 4÷6 | 2÷4 | 8÷10 | 4÷6 |
| Izod impact strength (3,2 mm) | |||||||||
| kJ/m2 J/m |
GOST 19109-84 ASTM D-256 (À) ISO 180 ASTM D-256 (À) |
10 102 | 15 152 | 27 274 | 25 254 |
35 356 | 40 406 | 12 122 | 6 61 |
| Vicat softening point (5 kg, 50°C/hr) | |||||||||
| °Ñ | GOST 15088-83 ASTM D-1525 |
97 | 98 | 94 | 93 | 90 | 88 | 85 | 104 |
| Tensile yield strength | |||||||||
| MPà | GOST 11262-80 ASTM D-638 |
38 | 42 | 36 | 34 | 32 | 30 | 34 | 50* |
| Relative elongation at break (20 mm/min) | |||||||||
| % | GOST 11262-80 ASTM D-638 |
30 | 15 | 25 | 20 | 40 | 60 | – | – |
| Gloss (60° angle) | |||||||||
| % | Plastpolymer method ASTM D-253 |
– | 75÷80 | – | – | – | – | – | – |
| Inflammability | |||||||||
| – | UL-94 | HB | HB | HB | HB | HB | HB | V-O | HB |
| Residual monomer content | |||||||||
| % | GOST 15820-82 – styrene – acrylonitrile |
0,05 0,001 | 0,05 0,001 | 0,05 0,001 | 0,05 0,001 |
0,05 0,001 | 0,05 0,001 | 0,05 0,001 | 0,05 0,001 |
| MFI range of one lot | |||||||||
| % | Plastpolymer method | ± 10 | ± 10 | ± 10 | ± 10 | ± 10 | ± 10 | ± 10 | ± 10 |
* Tensile strength (MPa) is indicated